Cast iron crack repair, metal fatigue failure, metal brittleness, metal crack regeneration, aluminum cracking.
We will repair the cracks that have occurred in the metal and machinery equipment without welding. This allows for the repair of metal cracks without causing thermal distortion.
The "MS Method (Mechanical Stitch)" is a groundbreaking repair technique (Mechanical Stitch Method) that uses mechanical methods to address cracks in metal. Since it does not apply any heat at all, there is no "thermal distortion." It prevents residual stress from occurring in other areas and also prevents secondary damage such as new cracks. Cracks in metal are one of the concerns in equipment maintenance operations. In general welding repair methods, the base material around the crack changes due to heat, leading to residual stress and distortion, which always carries the risk of "crack recurrence" and "secondary damage." 【Features of the MS Method】 ■ No hardening or residual stress from heat ■ Elimination of secondary damage ■ Maintenance of stable quality → Integrated system repairs using jigs, etc. → Accumulation of know-how, experience, and achievements ■ Completion of construction in a short period → Does not significantly reduce the operating rate of equipment ■ Advantages in safety and environmental aspects → Since no fire is used, there is no impact on the operating rate of other equipment or the environment For more details, please contact us.
basic information
The MS method for repairing metal cracks demonstrates outstanding effectiveness in terms of precision, durability, and cost compared to conventional methods. It is a technology that physically repairs cracks using our special bolts and reinforcement plates. Since it can be implemented on-site, it allows for reduced lead times and cost savings. We have experience in a wide range of fields, including cast iron cracks, marine equipment, power generation facilities, and cement equipment. Please feel free to contact us if you have any questions. 【Product Lineup】 ○ S Bolt → Ensures airtightness and removes cracks → Thoughtfully designed screw structure achieves pulling force on the base material ○ T Bolt → Prevents MS reinforcement plate from pulling out and patch repairs → Unique tapered section enhances airtightness and prevents loosening ○ MS Reinforcement Plate → Reinforces and restores the repair area → Suppresses the force that would cause cracks to spread and strongly reinforces the base material ○ MS Bolt Hole Repair Insert → Female screw part for reinforcing damaged bolt holes ・ HS Type Insert: When there are no cracks around the bolt hole ・ HF Type Insert: When there are cracks around the bolt hole
Price information
Please contact us.
Delivery Time
Applications/Examples of results
<Cement Plant Equipment Achievements> - Reduction Gear Casing - Support Roller - Kiln Tire - Cement Mill Cover - Cement Mill Body - Girth Gear <Power Generation Equipment Achievements> - Steam Turbine Casing - Gas Turbine Casing - Pump Casing - Boiler - Internal Combustion Engine Crankcase <Maritime Related Achievements> - Crankcase - Freshwater Cooler - Housing - Intake and Exhaust Pipes - Air Clutch Bolt Hole <Steelmaking and Iron and Steel Related Achievements> - Forging Press Frame - Cutting Machine - CRG - Cooling Tower Blade <General Industrial Machinery Achievements> - Motor Base - Casting Equipment - Press Machine Frame - Press Machine Crown - Bolster - Slide - Upright - Vibrating Screen - Feeder - Connecting Rod - Press Bed - Injection Molding Machine Link Housing <Others> - Casting Prototypes - Aluminum Prototypes - Casting Foundry - Foundry - Industrial Machinery Parts Manufacturing - Injection Molding Machine Mold Fixing Bolt Hole - Platen - Piano Soundboard - Casing Bolt Hole - Exhaust Pipe Bolt If you have any questions, please feel free to contact us.