Metal casting repair, screw hole repair, MS method, casting crack repair, crack regeneration.
Welding-free metal crack repair! We repair cracks without applying any heat! Cracks that occur in metal are repaired using mechanical methods!
The "MS Method (Mechanical Stitch)" is a groundbreaking repair technique (Mechanical Stitch Method) that addresses metal cracks using mechanical methods. Since no heat is applied at all, there is no "thermal distortion." Residual stress does not occur in other areas, preventing secondary damage such as new cracks. Metal cracks are one of the concerns in equipment maintenance operations. In typical welding repair methods, the base material around the crack changes due to heat, leading to residual stress and distortion, which constantly carries the risk of "crack recurrence" and "secondary damage." 【Features】 ■ No hardening or residual stress due to heat ■ Elimination of secondary damage ■ Maintenance of stable quality → Integrated system repairs with jigs and other tools → Accumulation of know-how, experience, and track record ■ Completion of construction in a short period → No significant reduction in the operating rate of equipment ■ Advantages in safety and environmental aspects → No use of fire, thus no impact on the operating rates of other equipment or the environment For more details, please contact us.
basic information
The MS method for repairing metal cracks demonstrates outstanding effectiveness in terms of precision, durability, and cost compared to conventional methods. It is a technology that physically repairs cracks using our special bolts and reinforcement plates. Since it can be implemented on-site, it allows for reduced lead times and cost savings. We have experience in a wide range of fields, including cast iron cracks, marine equipment, power generation facilities, and cement equipment. Please feel free to contact us if you have any questions. 【Product Lineup】 ○ S-Bolt → Ensures airtightness and removes cracks → Thoughtfully designed screw structure achieves tensile strength of the base material ○ T-Bolt → Prevents MS reinforcement plate from pulling out and patch repairs → Unique tapered section enhances airtightness and prevents loosening ○ MS Reinforcement Plate → Reinforces and restores the repair area → Suppresses the force that would cause cracks to spread and strongly reinforces the base material ○ MS Bolt Hole Repair Insert → Female threaded part for reinforcing damaged bolt holes ・ HS Type Insert: For cases where there are no cracks around the bolt hole ・ HF Type Insert: For cases where there are cracks around the bolt hole
Price information
Prices may vary depending on the crack condition, so please feel free to contact us.
Delivery Time
Applications/Examples of results
【Examples of Achievements】 <Achievements in Cement Plant Equipment> - Gearbox casing - Support roller - Kiln tire - Cement mill cover - Cement mill body - Girth gear <Achievements in Power Generation Equipment> - Steam turbine casing - Gas turbine casing - Pump casing - Boiler - Internal combustion engine crankcase <Achievements in Marine Related Equipment> - Crankcase - Freshwater cooler - Housing - Manifold - Intake and exhaust pipes - Air cooler bolt holes <Achievements in Steelmaking and Iron and Steel Related Equipment> - Forging press frame - Cutting machine - CRG - Cooling tower blades <Achievements in General Industrial Machinery> - Motor pedestal - Casting equipment - Press machine frame - Press machine crown - Bolster - Slide - Upright - Vibrating screen - Feeder - Connecting rod - Press bed - Casting machine - Forging machine - Die-cast frame - Injection molding machine link housing <Others> - Casting prototypes - Aluminum prototypes - Casting foundry - Foundry - Industrial machinery parts manufacturing - Injection molding machine mold fixing bolt holes - Platen - Piano soundboard - Casing bolt holes - Exhaust pipe bolts - Casting crack repair