Non-heat metal casting crack repair Mechanical Stitching Method "MS Method"
A new method for metal crack repair that shortens construction time, reduces costs, and does not apply heat! No thermal distortion because no heat is applied!
The "MS Method (Mechanical Stitch)" is a groundbreaking repair technique (Mechanical Stitching Method) that uses mechanical means to address cracks in metal. Since no heat is applied at all, there is no "thermal distortion." It prevents the generation of residual stress in other areas and also prevents secondary damage such as new cracks! In conventional welding repair methods, heat causes changes in the base material around the crack, leading to residual stress and distortion, which always carries the risk of "crack recurrence" and "secondary damage." 【Features of the MS Method】 ■ No hardening or residual stress due to heat ■ Elimination of secondary damage ■ Maintenance of stable quality → Integrated system repairs using jigs, etc. → Accumulation of know-how, experience, and track record ■ Completion of construction in a short period → Does not significantly reduce the operating rate of equipment ■ Advantages in safety and environmental aspects → No use of fire, thus no impact on the operating rate of other equipment or the environment *For more details, please contact us.
basic information
【Features】 ■ No distortion, hardening, or residual stress due to heat ■ High-precision repairs with no secondary damage ■ Maintenance of stable quality → Unlike welding repairs that require special skills, this is an integrated system repair → Stable quality can be maintained ■ Completion of work in a short period → Continuous work is possible, significantly reducing the downtime of equipment ■ Advantages in safety and environmental aspects → No use of fire, eliminating concerns about the operation of other equipment and materials regarding safety and the environment For more details, please contact us.
Price range
Delivery Time
Applications/Examples of results
【Cement Plant Equipment Achievements】 - Gearbox casing - Support roller - Kiln tire - Cement mill body - Girth gear 【Power Generation Equipment Achievements】 - Steam turbine casing - Gas turbine casing - Pump casing - Internal combustion engine crankcase 【Marine Related Achievements】 - Crankcase - Cylinder liner - Intake and exhaust pipes - Intercooler - Bracket 【Steel and Iron Related Achievements】 - Forging press frame - Coal raw material mill - Cutting machine - Cooling tower blades 【General Industrial Machinery Achievements】 - Intercooler mounting bolt holes - Applicator screw holes - Power vice - Machining table work fastening bolt holes - Cylinder head exhaust pipe mounting bolt holes - Motor base - Casting equipment - Press machine frame - Press machine crown - Press machine slide - Press machine upright - Press machine bed - Injection molding machine link housing - Injection molding machine platen - Connecting rod - Cone crusher - Platen screw holes - Mold mounting bolt holes - Platen die plate <If you have any other questions, please contact us.>
Detailed information
-
Crack condition confirmation Confirm the overall condition of the cracks. Consider construction methods based on the length and depth of the cracks and the factors that caused them.
-
S-bolt installation status for crack removal. S-bolts are installed for crack removal and fastening.
-
Installation status of the jig for processing holes in reinforcement plates. Reinforcement plates are installed perpendicular to the cracks.
-
Status of reinforcement plate hole processing Hole processing was carried out using a dedicated jig.
-
Status of reinforcement plate installation The reinforcement plate is being driven into the processed pilot hole.