Heat-resistant/Metal Repair/Build-up Putty Belzona 1511 Super HT Metal
A repair material for build-up that can withstand dry environments of 210°C or higher and can be machined after curing. [Applications] For repairs of heat exchangers, castings, tanks, etc.
[Overview] This is a heat-resistant repair material that is ideal for rebuilding base metals damaged by erosion and corrosion. After curing, it can be machined and adheres strongly to various metals. Like other products, it can be easily used by anyone simply by mixing the main agent and hardener in the appropriate ratio. *This product is not a hazardous substance. ＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝ [Demo/Sample Distribution] If you would like a demo or sample, please fill out the application with your intended use and conditions in the "Contact Us" section below and send it. *Please note that we may decline requests depending on various conditions. ＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝＝
basic information
[Procedure] □Surface Preparation: Remove rust from corroded metal areas using blasting or grinding, and roughen the surface. □Degreasing Cleaning: Remove moisture, oil, and dirt using a cleaning agent. □Mixing: Take the main agent and hardener in the specified mixing ratio on a board made of plastic or similar material and mix thoroughly to avoid color unevenness. □Application: Initially apply to the prepared surface by rubbing it in, then apply additional layers until the required thickness is achieved. *Depending on the temperature used, post-curing (forced heating curing) may be necessary. Please refer to the instruction manual for details. [Product Information] □Form: Paste "after mixing" □Color: Gray □Packaging: 1kg "main agent and hardener set" □Weight Mixing Ratio: Main agent 5 : Hardener 1 [Product Properties] □Adhesive Strength (Iron): 21.1 MPa □Heat Resistance Temperature: 210°C (dry) 150°C (wet)
Price range
P2
Delivery Time
P2
Model number/Brand name
Super HT Metal (Belzona 1511)
Applications/Examples of results
- Vessel - Heat exchanger - Piping - Tank - Casting - Flange face - Nozzle - Sleeve
Detailed information
-
Before the test ⇒ Condition after the test Test content: Left in the testing device for 72 hours under temperature 150℃ and 100% relative humidity conditions 【Common conditions for the sample】 - Sample size: 70mm × 150mm - Film thickness: approximately 1mm - Mixing ratio of base agent/hardener and curing time are according to catalog values - Base material used is SS material - Brush application was performed
-
Heat exchanger cover repair: It exhibits high adhesive strength even for high-temperature equipment, so high resistance can be expected.
-
Nozzle insert: Even the narrow inner surfaces of nozzles, which are difficult to coat, can be reliably protected from corrosion using the nozzle insert method.