Regarding the silicone corrosion resistance test.
![[Catalog] Silicoroika Catalog - Digest Edition (24P)](https://image.mono.ipros.com/public/premium/image_category/21b/114992/IPROS81237408795043183708.jpeg?w=140&h=140){kind=small}
![[Catalog] Silicoroi Technology Handbook Pro1 (164P)](https://image.mono.ipros.com/public/premium/image_category/21b/114992/IPROS94635557432701009129.jpeg?w=140&h=140){kind=small}
![[Catalog] Silicoroy Technology Handbook Pro2 (106P)](https://image.mono.ipros.com/public/premium/image_category/21b/114992/IPROS23850094675735515703.jpeg?w=140&h=140){kind=small}
![[Catalog] Silicoroy XVI MAST Hardon Plate Technical Documentation](https://image.mono.ipros.com/public/premium/image_category/21b/114992/IPROS35461915036482705305.jpeg?w=140&h=140){kind=small}
The sample is immersed in a 6% hydrochloric acid solution of ferrous chloride at room temperature for 96 hours, and the weight change before and after the test is measured.
We will introduce the resistance to pitting corrosion test of "SIRICOROI." First, prepare a test solution of 6% hydrochloric acid and ferric chloride solution. The test specimens are produced from various materials under different heat treatment conditions. The surface roughness is adjusted using waterproof sandpaper #400, and degreasing is performed with acetone. Then, each material is immersed in the 6% hydrochloric acid and ferric chloride solution at room temperature for 96 hours, and the weight change before and after the test is measured using a precision balance to determine the degree of corrosion. For more details, please download and view the catalog. [Test Specimens (Partial)] ■SUS304 ■SUS316L ■SUS420J2 ■SUS440C ■SUS630-H900 *For more details, please refer to the PDF materials or feel free to contact us.
basic information
【Other Test Specimens (Partial)】 ■ Maraging Steel - AG ■ Silicoroy A2 - AG ■ Silicoroy XVI - DAG ■ Silicoroy XVI - ST ■ Silicoroy B2 *For more details, please refer to the PDF materials or feel free to contact us.
Price range
Delivery Time
Applications/Examples of results
For more details, please refer to the PDF document or feel free to contact us.