PLA-based multifunctional graft polymer SCONA TPPL series
Graft polymer with various functional groups grafted onto polylactic acid (PLA)
Features ✓ Graft polymer with various functional groups grafted onto polylactic acid (PLA) ✓ Functional groups tailored for specific applications (modification purposes) Maleic anhydride, acrylic acid, glycidyl methacrylate SCONA TPPL 1214 PA: Viscosity modifier, melt tension enhancer, compatibilizer, coupling agent SCONA TPPL 1310 PA: Melt viscosity modifier/melt tension enhancer, (synergist for chain-extended epoxy) dispersant SCONA TPPL 1112 PA: Coupling agent for fillers and fibers, compatibilizer SCONA TPPL 5112 PA: Coupling agent, compatibilizer, dispersant for high-flow fillers and fibers
basic information
- SCONA TPPL 1214 PA Graft functionality: Glycidyl methacrylate Graft level: > 2.5 % Dry weight loss (180 min, 110 °C): < 0.5 % - SCONA TPPL 1310 PA Graft functionality: Acrylic acid Graft level: > 3.0 % MVR (190 °C, 2.16 kg): 3–10 cm³/10 min Dry weight loss (180 min, 110 °C): < 0.8 % - SCONA TPPL 1112 PA Graft functionality: Maleic anhydride Graft level: > 1.0 % MVR (190 °C, 2.16 kg): 1–8 cm³/10 min Dry weight loss (180 min, 110 °C): < 0.5 % - SCONA TPPL 5112 PA Graft functionality: Maleic anhydride Graft level: > 1.0 % MVR (190 °C, 2.16 kg): 20–30 cm³/10 min Dry weight loss (180 min, 110 °C): < 0.5 %
Price information
Please contact us for the price.
Delivery Time
Model number/Brand name
DISPERBYK, BYK
Applications/Examples of results
Main proposed applications - Reinforcement enhancement of fillers and natural fiber reinforced compounds (such as PLA, PBS, PBAT) - Compatibility of different bio-based polymers - Viscosity adjustment of bio-based compounds (such as extrusion molding, blow molding, foam molding)